EN 10025-2 S235J2 Mild steel plate

Low temperature impacting test shall be done for EN 10025-2 S235J2 Mild steel plate under minus 20 centigrade.

When rolling of steel plate S235J2, as rolled or Normalizing rolling is both ok. As rolled delivery condition without any special rolling and heat treatment condition.

Normalizing rolling process in which the final deformation is carried out in a certain temperature range leading to a material condition equivalent to that obtained after normalizing so that the specified values of the mechanical properties are retained even after Normalized.

EN 10025-2 S235J2 steel Chemical Composition:

Steel grade	C max. %	Mn max. %	Si max. %	P max. %	S max. %	N max. %	Cu max. %	Other max. %
S235J0	0,17	1,40	-	0,030	0,030	-	0,55	-

EN 10025-2 S235J2 steel Mechanical Property:

Minimum yield strength Reh
MPa

Tensile strength Rm
MPa

Minimum elongation - A
Lo = 5,65 * √So (%)

Notch impact test

Steel grade

Nominal thickness
mm

Temperature

Min. absorbed energy

≤16

>16
≤40

>40
≤63

>63
≤80

>80
≤100

>100
≤125

>3
≤100

>100
≤125

>3
≤40

>40
≤63

>63
≤100

>100
≤125

°C

S235J2

235

225

215

195

360-510

350-500

-20

Main application of S235J2 is firstly and largely producing structural parts of the bolted and welded steel industrial area.