Welding requirements of NM550 wear plate

(1) Preheating measures are taken before welding to ensure that the preheating temperature of NM550 wear-resistant steel plate is ≥ 200 °C.

(2) The NM550 wear-resistant plate should be cleaned of oil, rust and other dirt within the range of 30~50 mm from both sides of the groove before welding.

(3) It is recommended to use low-hydrogen and ultra-low-hydrogen welding materials for welding NM550 wear-resistant plate. Solid wire is recommended for CO2 welding, Low-strength welding materials are not prone to low-temperature cracking (hydrogen-induced cracking).

(4) Dry the manual arc welding electrode of the NM550 wear-resistant plate at 350 ℃, keep it warm for 1~2 hours after the drying temperature reaches, and take it as needed.

(5) In the process of welding NM550 wear-resistant plates, control the temperature between welding layers to be ≥200°C.

(6) After welding, take asbestos insulation for the NM550 wear-resistant plate weld to make it cool slowly.

Message

You can fill out the form below for your information needs, our technical and sales staff will get in touch with you. To ensure timely processing of your information, be sure to accurately fill out your contact phone!

* Name :
* Email :
* Tel :
* Message :	If the above information does not meet your needs, please fill in your specific needs here.