ASTM A202 Pressure Vessel Hot Rolled Plates Price

ASTM A202 material has two common variants (Grade A and B), each represented as a separate material. This specification dedigns Chromium-Manganese-Silicon alloy steel plates. This alloy is intended mainly for welded boilers and other pressure vessels. The maximum thickness for the plates is limited under this standard to 2in. [50mm]. Grade A is suitable for rivets and when so used the bars shall be subjected to the requirements fot hot rolled bars specified in the specification.

Availabe Size: Thickness: 4mm- 220mm;
Width: 1000mm- 4000mm;
Length: 4000mm- 12000mm.
Production ability:1000 Tons Per Month.
Production Way: Hot Rolled
ASTM A202 Plates Physical Properties:
Base Metal Price3.5 % rel
Density: 7.8 g/cm3 (490 lb/ft3)
Elastic (Young's, Tensile) Modulus: 210 GPa (30 x 106 psi)
Elongation at Break: 17 to 18 %
Modulus of Resilience (Unit Resilience): 310 to 330 kJ/m3
Poisson's Ratio: 0.29
Specific Heat Capacity: 450 J/kg-K
Strength to Weight Ratio: 76 to 86 kN-m/kg
Tensile Strength: Ultimate (UTS): 590 to 670 MPa (86 to 97 x 103 psi)
Tensile Strength: Yield (Proof): 360 to 370 MPa (52 to 54 x 103 psi)
Thermal Expansion: 12 µm/m-K
Unit Rupture Work (Ultimate Resilience): 87 to 88 MJ/m3
BEBON STEEL will offer you the prime quality ASTM A202 hot rolled plates with competitive price. We also provide this product with cutting, welding, forming and testing service.