Contact us
- : 0086-371-86151627 0086-371-86151827
- : 0086-371-86011881
- : [email protected]
- : [email protected]
- : bebonchina
Products- Boiler steels
- High carbon steel
- High Yield steel
- steel for welded tubes
- General construction steel
- steel with Cr.,Mo.,Cr-Mo
- Steel for large diameter pipes
- Simple pressure vessels steel
- Steel for gas cylinders and gas vessels
- General purpose structural steels
- Steel for boilers and pressure vessels
- steel resistant to atmospherical corrosion
- Carbon steel and low alloy steel
- Fine-grain structural steels,normalised rolled
- weldable normalized fine grained pressure vessel steels
News- Heavy-Forging Thick Steel Plates for
- Marine-Grade Thick Steel Plates for
- Storage Tank Thick Steel Plates for
- Seismic-Resistant Thick Steel Plates
- Extra-Wide Thick Steel Plates for La
- Clad Thick Steel Plates with Stainle
- HIC-Resistant Thick Steel Plates for
- Low-Temperature Thick Steel Plates f
- Thick Steel Plates for Offshore Wind
- Thick Steel Plates in Cement Product
European standard pressure vessel steel P355NH plate
P355NH European standard pressure vessel steel plate is a weldable fine grain steel. P355NH executive standard: EN10028. It belongs to low alloy high strength steel. P355NH plate is widely used in petroleum, chemical, power station, boiler and other industries.
P355NH pressure vessel steel plate chemical composition elements, melting analysis:
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | Nb | V | Ti | Alt | N |
| ≤0.18 | ≤0.5 | 1.1-1.7 | ≤0.025 | ≤0.015 | ≤0.5 | ≤0.3 | ≤0.08 | ≤0.3 | ≤0.05 | ≤0.1 | ≤0.03 | ≥0.02 | ≤0.012 |
Composition note: Nb+Ti+V≤0.12; Cr+Cu+Mo≤0.45. Ceq = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
P355NH steel longitudinal impact, mechanical properties:
P355NH plate delivery status: Normalized.
| Thickness | Mechanical properties | ||
| <5 | ReH(MPa) | ≥355 | |
| Rm(MPa) | 490-630 | ||
| A(%) | ≥22 | ||
| 5-16mm | ReH(MPa) | ≥355 | |
| Rm(MPa) | 490-630 | ||
| A(%) | ≥22 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
| >16-40 | ReH(MPa) | ≥345 | |
| Rm(MPa) | 490-630 | ||
| A(%) | ≥22 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
| >40-60 | ReH(MPa) | ≥335 | |
| Rm(MPa) | 490-630 | ||
| A(%) | ≥22 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
| >60-100 | ReH(MPa) | ≥315 | |
| Rm(MPa) | 470-610 | ||
| A(%) | ≥21 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
| >100-150 | ReH(MPa) | ≥305 | |
| Rm(MPa) | 460-600 | ||
| A(%) | ≥21 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
| >150-250 | ReH(MPa) | ≥295 | |
| Rm(MPa) | 450-590 | ||
| A(%) | ≥21 | ||
| Impact temperature | -20 | ||
| Akv(J) | ≥45 | Longitudinal; Transverse: Akv ≥ 30J | |
Tensile properties of P355NH plate:
The tensile strength range of P355NH steel plate is Rm630-450MPa. The yield strength is above 355-295MPa (less than or equal to 16 mm). The elongation after fracture is 21-22%.