- : 0086-371-86151627 0086-371-86151827
- : 0086-371-86011881
- : [email protected]
- : [email protected]
- : bebonchina
- Boiler steels
- High carbon steel
- High Yield steel
- steel for welded tubes
- General construction steel
- steel with Cr.,Mo.,Cr-Mo
- Steel for large diameter pipes
- Simple pressure vessels steel
- Steel for gas cylinders and gas vessels
- General purpose structural steels
- Steel for boilers and pressure vessels
- steel resistant to atmospherical corrosion
- Carbon steel and low alloy steel
- Fine-grain structural steels,normalised rolled
- weldable normalized fine grained pressure vessel steels
- The process of Production and Cuttin
- Advantages of lowering hot rolling t
- Reliable strength and quality with s
- The purpose of tempering 30CrMo stee
- Chemical Composition of 30CrMo Steel
- Carburizing Process of 30CrMo Steel
- ASTM A242 steel VS A588: which is be
- A242 steel plate: properties and app
- Rolling points of HP325 Steel
- Causes of Wrinkles on the Surface of
Advantages of lowering hot rolling temperature on S355MC steel
Due to the sensitivity of S355MC steel to high temperature, what is the advantage of lowering the rolling temperature for S355MC steel during hot rolling?
(1)Reducing the hot rolling temperature can significantly increase the elongation and area reduction of S355MC steel, and reduce the yield strength, while the tensile strength of S355MC steel is only slightly reduced.
(2)The metallographic microstructure shows that reducing the rolling temperature can reduce the reticular ferrite and massive ferrite, and is beneficial to the homogenization of the ferrite and pearlite structures of S355MC steel.
(3)The fracture morphology shows that reducing the rolling temperature can increase the tear ribs and dimples, thereby homogenizing the fracture zone and improving the toughness of S355MC steel.
(4) The displacement of ferrite growing into the crystal is related to the austenite transformation temperature and transformation time. Lowering the rolling temperature can refine the ferrite structure of S355MC steel.