- : 0086-371-86151627 0086-371-86151827
- : 0086-371-86011881
- : [email protected]
- : [email protected]
- : bebonchina
- Boiler steels
- High carbon steel
- High Yield steel
- steel for welded tubes
- General construction steel
- steel with Cr.,Mo.,Cr-Mo
- Steel for large diameter pipes
- Simple pressure vessels steel
- Steel for gas cylinders and gas vessels
- General purpose structural steels
- Steel for boilers and pressure vessels
- steel resistant to atmospherical corrosion
- Carbon steel and low alloy steel
- Fine-grain structural steels,normalised rolled
- weldable normalized fine grained pressure vessel steels
- Application fields of 30CrMnSi steel
- 30CrMnSi steel heat treatment proces
- Cost-efficient choice: affordable pr
- Budget-friendly option: competitive
- Rolling points of HP295 Steel
- Causes of Wrinkles on the Surface of
- Advantages of Controlled Rolling for
- What is the difference between 304 s
- 201 Stainless steel vs 202 Stainless
- Is 201 stainless steel food grade?
30CrMnSi steel heat treatment process specification
30CrMnSi steel is a high-strength quenched and tempered structural steel with high strength and toughness, medium cold deformation plasticity, good machinability, and good weldability (but when the thickness is greater than 3mm, it should be preheated to 150°C before welding. Heat treatment), high hardenability, easy to produce white spots, decarburization tendency, temper brittleness in the range of 250-380°C and 460-650°C, poor transverse impact toughness, can be used for low-temperature tempering, or Use after high temperature tempering, tempering above 550°C has higher impact toughness (in order to improve toughness, reduce deflection and deformation, small cross-section parts can be austempered at 350°C to obtain lower bainite structure, but the cooling of austempering The temperature of the medium should not be too high, otherwise the impact toughness will be reduced.)
30CrMnSi steel is mostly used to manufacture various important parts with high load and high speed, such as gears, shafts, clutches, sprockets, grinding wheel shafts, bushings, bolts, nuts, etc., and is also used to manufacture wear-resistant, low-temperature parts and Welded components with variable loads, such as blades and valve plates of high-pressure blowers and pipes for non-corrosive piping.