Contact us
- : 0086-371-86151627 0086-371-86151827
- : 0086-371-86011881
- : [email protected]
- : [email protected]
- : bebonchina
Products- Boiler steels
- High carbon steel
- High Yield steel
- steel for welded tubes
- General construction steel
- steel with Cr.,Mo.,Cr-Mo
- Steel for large diameter pipes
- Simple pressure vessels steel
- Steel for gas cylinders and gas vessels
- General purpose structural steels
- Steel for boilers and pressure vessels
- steel resistant to atmospherical corrosion
- Carbon steel and low alloy steel
- Fine-grain structural steels,normalised rolled
- weldable normalized fine grained pressure vessel steels
News- Rolling points of HP265 Steel
- Causes of Wrinkles on the Surface of
- Advantages of Controlled Rolling for
- The difference between A283 Gr C and
- Quality inspection of plate A285 gra
- A285 Gr.C plate for storage tanks
- The processing Technology of NM400 S
- Possible defects of 16Mo3 steel plat
- Acceptance criteria of Surface for 1
- Heat Treatment and Applications of A
Production technology of SA737 grade C steel plate
SA737 grade C steel plate smelting process: open hearth, oxygen blowing converter or electric furnace. The steel shall be killed and meet the requirements for fine austenite grain size in the A20/A20M standard.
The SA737 gr C steel material is heated to an appropriate temperature for normalizing to form an austenite structure, but the temperature should not exceed 925, and it should be maintained at this temperature for a sufficient time to make the entire material uniformly heated, and then cooled in air.
If the buyer agrees, in order to improve the strength or toughness, the cooling rate is allowed to be faster than air cooling, but then the SA737 grade C steel plate must be tempered in the range of 95-705.